Cavitated - Pearlized and White

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
H1-PLC Pearl White Low COF Low Heat Sealable One Side Corona Treated 20 TO 45 µ
  • Ultra Low COF Low Heat Seal Untreated Side
  • Excellent Opacity
  • Low Seal Initiation Temperature
  • Excel ent Hot Tack and Heat Seal Strength
  • Brilliant Pearlicent White Appearance
  • Very Good Barrier Properties
  • High Surface Gloss
  • Excel ent Surface Treatment Retention
  • Excel ent Anchorage of Inks and Lamination Adhesive on Treated Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines *Available in Inside / Outside Corona Treated, as per the requirement of the customer
Pearl White Low Heat Sealable Ultra Low COF One Side Corona Treated Film for Very High Speed Confectionary Packing Application. Also Very Useful for other single / two Ply High Speed Printing, Lamination & Pouching Applications.  
H1-PLS 20 TO 40 µ
  • Excellent Opacity
  • Low Seal Initiation Temperature
  • Excellent Hot Tack and Heat Seal Strength
  • Brilliant Pearlicent White Appearance
  • Very Good Barrier Properties
  • High Surface Gloss
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Inks and Lamination Adhesive on Treated Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
  • Available in Inside / Outside Corona Treated, as per the requirement of the customer
Pearl White Low Heat Sealable One Side Corona Treated Film for Ice Cream Packaging. Also Useful Other single / two Ply Printing Lamination Application  
H1-PL Pearl White Both Side Heat Sealable One Side Corona Treated 20 TO 40 µ
  • Excellent Opacity
  • Brilliant Pearlicent White Appearance
  • Very Good Barrier Properties
  • High Surface Gloss
  • Excellent Hot Tack and Heat Seal Strength
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Inks and Lamination Adhesive on Treated Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
  • Available in Inside / Outside Corona Treated, as per the requirement of the customer
Pearl White Both Side Heat Sealable One Side Corona Treated Film for single / two Ply Printing Lamination Application  
H1-PUL Pearl White Ultra Low Heat Sealable One Side Corona Treated 25 TO 40 µ
  • Excellent Opacity
  • Ultra Low Seal Initiation Temperature
  • Excellent Hot Tack and Heat Seal Strength
  • Brilliant Pearlicent White Appearance
Pearl White Ultra Low Heat Sealable One Side Corona Treated Film  

THERMAL GLOSS FINISH BOPP FILM

Application:

Pearl White Low Heat Sealable Ultra Low COF One Side Corona Treated Film for Very High Speed Confectionary Packing Application. Also Very Useful for other single / two Ply High Speed Printing, Lamination & Pouching Applications.

Description:

Pearl White Low COF Low Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PLC
Pearl White Low COF Low Heat Sealable One Side Corona Treated
Pearl White Low Heat Sealable Ultra Low COF One Side Corona Treated Film for Very High Speed Confectionary Packing Application. Also Very Useful for other single / two Ply High Speed Printing, Lamination & Pouching Applications. Pearl White, Low Heat Sealable, Ultra Low COF, One Side Corona Treated OPP Film with Very Good Barrier, Outstanding Slip and Antistatic Properties for use in Single / Two Ply Printing Lamination Application, Specifically for High Speed Confectionary Packaging Application. Ultra Low COF untreated side facilitate the smooth running of film on confectionary packaging machine at minimum speed of 1200 packs/min. The corona treated side is specifically designed for excel ent adhesion of inks and lamination adhesives. Untreated side exhibits Ultra Low COF, low seal initiation temperature, excel ent hot tack and seal strength.

THERMAL GLOSS FINISH BOPP FILM

Application:

Pearl White Low Heat Sealable One Side Corona Treated Film for Ice Cream Packaging. Also Useful Other single / two Ply Printing Lamination Application

Description:

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PLS
Pearl White Low Heat Sealable One Side Corona Treated Film for Ice Cream Packaging. Also Useful Other single / two Ply Printing Lamination Application Pearl White, Low Heat Sealable, One Side Corona Treated OPP Film with Very Good Barrier, Slip and Antistatic Properties for use in Single / Two Ply Printing Lamination Application, Specifically for Ice cream Packaging Application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesives. Untreated side exhibits ultra low seal initiation temperature, excellent hot tack and seal strength

THERMAL GLOSS FINISH BOPP FILM

Application:

Pearl White Both Side Heat Sealable One Side Corona Treated Film for single / two Ply Printing Lamination Application

Description:

Pearl White Both Side Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PL
Pearl White Both Side Heat Sealable One Side Corona Treated
Pearl White Both Side Heat Sealable One Side Corona Treated Film for single / two Ply Printing Lamination Application Pearl White, Both Side Heat Sealable, One Side Corona Treated OPP Film with Very Good Barrier, Slip and Antistatic Properties for use in Single / Two Ply Printing Lamination Application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesives. Untreated side exhibits excellent hot tack and seal strength

THERMAL GLOSS FINISH BOPP FILM

Application:

Pearl White Ultra Low Heat Sealable One Side Corona Treated Film

Description:

Pearl White Ultra Low Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PUL
Pearl White Ultra Low Heat Sealable One Side Corona Treated
Pearl White Ultra Low Heat Sealable One Side Corona Treated Film Pearl White Ultra Low Heat Sealable One Side Corona Treated