Opaque White

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
H1-OP Opaque White Both Side Heat Sealable One Side Corona Treated 15 TO 45 µ
  • Excellent Opacity
  • Brilliant White Appearance
  • Very Good Barrier Properties
  • High Surface Gloss
  • Excellent Hot Tack and Heat Seal Strength
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Inks and Lamination Adhesive on Treated Side
  • Excellent Machinability,
  • Suitable for Various Printing / Lamination Machines *Available in Inside / Outside Corona Treated, as per the requirement of the customer
Opaque White Both Side Heat Sealable One Side Corona Treated Film for Single / Two Ply Printing Lamination Application  

THERMAL GLOSS FINISH BOPP FILM

Application:

Opaque White Both Side Heat Sealable One Side Corona Treated Film for Single / Two Ply Printing Lamination Application

Description:

Opaque White Both Side Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-OP
Opaque White Both Side Heat Sealable One Side Corona Treated
Opaque White Both Side Heat Sealable One Side Corona Treated Film for Single / Two Ply Printing Lamination Application Opaque White, Both Side Heat Sealable, One Side Corona Treated OPP Film with Very Good Slip and Antistatic Properties for use in Single / Two Ply Printing Lamination Application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesives. Untreated side exhibits excellent hot tack and seal strength