MET-PET

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
J950MO Normal density metallised direct matte polyester film with medium surface gloss. 12,23,36,50 µ
  • Standard density
  • Medium surface gloss
  • Good dimensional / thermal stability.
  • Excellent Machinability
labels and other industrial application.  
J952M1 Normal density Metallisation on translucent direct matte polyester film and other side corona treated 12,23,36,50 µ
  • Standard Density
  • Excellent Dimensional / Thermal Stability.
  • Excellent Machinability
  • Suitable for Printing
labels and other industrial application.  
J951M0 Normal density Metallised direct matte one side metallised and other side chemically coated. 12 µ
  • Standard Density
  • Good Dimensional / Thermal Stability.
  • Excellent Machinability
  • Suitable for Printing & Lamination
labels and other industrial application.  

THERMAL GLOSS FINISH BOPP FILM

Application:

labels and other industrial application.

Description:

Normal density metallised direct matte polyester film with medium surface gloss.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J950MO
Normal density metallised direct matte polyester film with medium surface gloss.
labels and other industrial application.

THERMAL GLOSS FINISH BOPP FILM

Application:

labels and other industrial application.

Description:

Normal density Metallisation on translucent direct matte polyester film and other side corona treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J952M1
Normal density Metallisation on translucent direct matte polyester film and other side corona treated
labels and other industrial application.

THERMAL GLOSS FINISH BOPP FILM

Application:

labels and other industrial application.

Description:

Normal density Metallised direct matte one side metallised and other side chemically coated.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J951M0
Normal density Metallised direct matte one side metallised and other side chemically coated.
labels and other industrial application.