Transparent Non Heat Sealable

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
N1 Transparent Non Heat Sealable One Side Corona Treated 8 to 50 µ
  • High Surface Gloss and Transparency
  • Excellent Clarity
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Inks and Lamination Adhesive on Treated Side
  • Excellent Machinability
  • Very Good Barrier Properties
  • Suitable for Various Printing / Lamination Machines
Book Covers Etc. This Film Is Also Suitable for Cold Seal Application.  
N2 Transparent Non Heat Sealable Both Side Corona Treated 8 to 50 µ
  • High Surface Gloss and Transparency
  • Excellent Clarity
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Inks and Lamination Adhesive
  • Excellent Machinability
  • Very Good Barrier Properties
  • Suitable for Various Printing / Lamination Machines
Reverse Printing and Lamination for Packaging Applications, Lamination of Printed Paper Boards / Posters / Book Covers Etc.  

THERMAL GLOSS FINISH BOPP FILM

Application:

Book Covers Etc. This Film Is Also Suitable for Cold Seal Application.

Description:

Transparent Non Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1
Transparent Non Heat Sealable One Side Corona Treated
Book Covers Etc. This Film Is Also Suitable for Cold Seal Application. Transparent, Non Heat Sealable, One Side Corona Treated, High Glossy OPP Film with Excellent Clarity, Slip and Antistatic Properties for use in Printing and Lamination Application. The Corona treated side is specifically designed for Excellent Adhesion of Inks and Lamination Adhesives.

THERMAL GLOSS FINISH BOPP FILM

Application:

Reverse Printing and Lamination for Packaging Applications, Lamination of Printed Paper Boards / Posters / Book Covers Etc.

Description:

Transparent Non Heat Sealable Both Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N2
Transparent Non Heat Sealable Both Side Corona Treated
Reverse Printing and Lamination for Packaging Applications, Lamination of Printed Paper Boards / Posters / Book Covers Etc. Transparent, Non Heat Sealable, Both Side Corona Treated, High Glossy OPP Film with Excellent Clarity, Slip and Antistatic Properties for use in Printing and Lamination Application. The Corona treated sides are specifically designed for Excellent Adhesion of Inks and Lamination Adhesives