MET-BOPP

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
H1-MD One Side Metallised, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits excellent water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The untreated heatsealable side exhibits excellent hot-tack and seal strength 15,18,20,25,30,35,40 µ
  • Excellent Surface Gloss on Metallised Side
  • Very Good Water Vapour and Gas Barrier Properties
  • Excellent Adhesion of Aluminium
  • Very Good Anchorage of Lamination Adhesive on Metallised Side
  • Very Good Metal Bond Strength
  • Very Good Lamination Bond Strength
  • Excellent Machinability
  • Very Good Hot-Tack and Seal Strength
Heat Sealable Metallised Film for Single / Two Ply Packaging Structure  
H1-LMD One Side Metallised, Other Side Low SIT Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure for High Speed Packaging Machines. The film exhibits excellent water vapour and gas barrier properties. During metal isation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives.The untreated low SIT heat sealable side exhibits excellent hot-tack and seal strength. 15,18,20,25,30,35,40 µ
  • Low SIT Heat Sealable Skin with Excellent Hot-tack and Seal Strength
  • Excellent Surface Gloss on Metallised Side
  • Very Good Water Vapour and Gas Barrier Properties
  • Excellent Adhesion of Aluminium
  • Very Good Anchorage of Lamination Adhesive on Metallised Side
  • Very Good Metal Bond Strength
  • Very Good Lamination Bond Strength
  • Excellent Machinability
  • Very Good Hot-Tack and Seal Strength
Low SIT Heat Sealable Metallised Film for Single / Two Ply Packaging Structure for High Speed Packaging Application.  
H1-UMD One Side Metallised, Other Side Ultra Low SIT Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure for High Speed Packaging Machines. The film exhibits excellent water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The untreated ultra low SIT heat sealable side exhibits excel ent hot-tack and seal strength. 15,18,20,25,30,35,40 µ
  • Ultra Low SIT Heat Sealable Skin with Excellent Hot-tack and Seal Strength
  • Excellent Surface Gloss on Metallised Side
  • Very Good Water Vapour and Gas Barrier Properties
  • Excellent Adhesion of Aluminium
  • Very Good Anchorage of Lamination Adhesive on Metallised Side
  • Very Good Metal Bond Strength
  • Very Good Lamination Bond Strength
  • Excellent Machinability
  • Very Good Hot-Tack and Seal Strength
Ultra Low SIT Heat Sealable Metallised Film for Single / Two Ply Packaging Structure for Very High Speed Packaging Applications  
N1-MD One Side Metallised, Other Side Non Heat Sealable OPP Film for use in Lamination with Paper / Paper Board, Gift Wrapping and Decorative Application. The film exhibits excellent water vapour and gas barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with Inks during printing. 8,10,15,17,18,20,25 µ
  • Excellent Surface Gloss on Metallised Side
  • Very Good Water Vapour and Gas Barrier Properties
  • Excellent Adhesion of Aluminium
  • Very Good Anchorage of Inks on Metallised Side
  • Very Good Metal Bond Strength
  • Excellent Machinability
Lamination with Paper / Paper Board for Various Applications like Disposable Paper Plates, File Covers, Leaflats Etc. • Gift Wrapping Applications • Other Decorative Applications  
N2-MD One Side Metallised, Other Side Corona Treated Non Heat Sealable OPP Film for use as Sandwich Layer in Three Ply Laminate Packaging Structure. The film exhibits excel ent water vapour and gas barrier properties. During metal isation process film is treated with plasma for enhancing metal adhesion and barrier properties. Metal ised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The corona treated non heat sealable side is also designed for excellent anchoring to lamination adhesive. 15,18,20,25,30,35,40,49 µ
  • Excellent Surface Gloss on Metallised Side
  • Excellent Water Vapour and Gas Barrier Properties
  • Excellent Adhesion of Aluminium
  • Very Good Anchorage of Lamination Adhesive on Metallised Side as wel as Corona Treated Side
  • Very Good Metal Bond Strength
  • Very Good Lamination Bond Strength
  • Excellent Machinability
Non Heat Sealable Metallised Film for Sandwich Layer in Three Ply Laminate Packaging Structure.  
H1-MTD One Side Matt Metallised, Other Side Heat Sealable OPP Film is excellent water vapour and gas barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The untreated heat sealable side exhibits excellent hot-tack and seal strength. 18 µ
  • Designed to give Rich Matt finish appearance after Metallization
  • Excellent Surface Treatment Retention
  • Excellent Adhesion of Aluminium on Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
  • Very Good Hot-Tack and Seal Strength
Heat Sealable Matt Metallised Film For High Speed Packaging Application.  
H1-PLD High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. For better anchorage of inks & lamination adhesives, a primer or corona booster may be applied on metallised side before conversion. The untreated heat sealable side exhibits excellent hot-tack and seal strength. 25,30,35,38,40,50 µ
  • Very High Water Vapour and Gas Barrier Properties
  • Excellent Opacity
  • One Side Brilliant Pearlescent White Appearance and Other Side Brilliant Metallic Lustre
  • Very High Surface Gloss
  • Low Seal Initiation Temperature
  • Excellent Hot Tack and Heat Seal Strength
  • For better anchorage of inks & lamination adhesives, a primer or corona booster may be applied on metallised side before conversion
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
White Cavitated Heat Sealable Metallised Film for Single / Two Ply Printing Lamination Application (For Ice Cream Packaging, Labels, High Value Food Packaging Etc.)  
H1-PDB High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single /Two Ply Packaging Structure. The film exhibits very high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with Inks and lamination adhesives. The untreated heat sealable side exhibits excellent hot-tack and seal strength. 25,30,35,38,40,50 µ
  • Very High Water Vapour and Gas Barrier Properties
  • Excellent Opacity
  • One Side Brilliant Pearlicent White Appearance and Other Side Brilliant Metallic Lustre
  • Very High Surface Gloss
  • Low Seal Initiation Temperature
  • Excellent Hot Tack and Heat Seal Strength
  • Excellent Surface Treatment Retention on Metallised Side
  • Excellent Anchorage of Inks and Lamination Adhesive on Metallised Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
High Barrier White Cavitated Heat Sealable Metallise Ed Film For Single / Two Ply Printing Lamination Application ( for Ice Cream Packaging, Labels, High Value Food Packaging Etc).  
H1-MDB High Barrier, One Side Metallized, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits very high water vapor and gas barrier properties. During metallization process film is treated with plasma for improving metal adhesion and barrier properties. Metallized side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. Untreated heat sealable side exhibits excellent hot-tack and seal strength. 15,18,20,25,30,35,40 µ
  • Very High Water Vapour and Gas Barrier Properties
  • Excellent Surface Gloss on Metallised Side
  • Excellent Adhesion of Aluminium on Treated Side
  • Very Good Anchorage of Lamination Adhesive on Metallised Side
  • Very Good Metal Bond Strength
  • Very Good Lamination Bond Strength
  • Excellent Machinability
  • Very Good Hot-Tack and Seal Strength
High Barrier Heat Sealable Metallised Film for Single / Two Ply Packaging Structure  
H1-AMD One Side Metallised, Other Side High Heat Seal Strength Sealable OPP Film for Use in Single / Two Ply Packaging Structure. Speciality of this Film is Very High Sealing Strength and Outstanding Hot Tack Properties. Due to the Excellent Sealing Characteristics, this film can be considered as potential Replacement of Metallised CPP in Two Ply Laminating Structure. Also, this film exhibits excellent water vapour and gas barrier properties compare to Metallised CPP. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. 18,20 µ
  • Very High Sealing Strength and Outstanding Hot Tack Properties
  • Excellent Surface Gloss on Metallised Side
  • Very Good Water Vapour and Gas Barrier Properties
  • Excellent Adhesion of Aluminium
  • Very Good Anchorage of Lamination Adhesive on Metallised Side
  • Very Good Metal Bond Strength
  • Very Good Lamination Bond Strength
  • Excellent Machinability
  • Very Good Hot-Tack and Seal Strength
High Heat Seal Strength Sealable Metallised Film for Single / Two Ply Packaging Structure. Potential Replacement of Metallised CPP in few Structures.  

THERMAL GLOSS FINISH BOPP FILM

Application:

Heat Sealable Metallised Film for Single / Two Ply Packaging Structure

Description:

One Side Metallised, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits excellent water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The untreated heatsealable side exhibits excellent hot-tack and seal strength

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-MD
One Side Metallised, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits excellent water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The untreated heatsealable side exhibits excellent hot-tack and seal strength
Heat Sealable Metallised Film for Single / Two Ply Packaging Structure

THERMAL GLOSS FINISH BOPP FILM

Application:

Low SIT Heat Sealable Metallised Film for Single / Two Ply Packaging Structure for High Speed Packaging Application.

Description:

One Side Metallised, Other Side Low SIT Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure for High Speed Packaging Machines. The film exhibits excellent water vapour and gas barrier properties. During metal isation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives.The untreated low SIT heat sealable side exhibits excellent hot-tack and seal strength.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-LMD
One Side Metallised, Other Side Low SIT Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure for High Speed Packaging Machines. The film exhibits excellent water vapour and gas barrier properties. During metal isation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives.The untreated low SIT heat sealable side exhibits excellent hot-tack and seal strength.
Low SIT Heat Sealable Metallised Film for Single / Two Ply Packaging Structure for High Speed Packaging Application.

THERMAL GLOSS FINISH BOPP FILM

Application:

Ultra Low SIT Heat Sealable Metallised Film for Single / Two Ply Packaging Structure for Very High Speed Packaging Applications

Description:

One Side Metallised, Other Side Ultra Low SIT Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure for High Speed Packaging Machines. The film exhibits excellent water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The untreated ultra low SIT heat sealable side exhibits excel ent hot-tack and seal strength.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-UMD
One Side Metallised, Other Side Ultra Low SIT Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure for High Speed Packaging Machines. The film exhibits excellent water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The untreated ultra low SIT heat sealable side exhibits excel ent hot-tack and seal strength.
Ultra Low SIT Heat Sealable Metallised Film for Single / Two Ply Packaging Structure for Very High Speed Packaging Applications

THERMAL GLOSS FINISH BOPP FILM

Application:

Lamination with Paper / Paper Board for Various Applications like Disposable Paper Plates, File Covers, Leaflats Etc. • Gift Wrapping Applications • Other Decorative Applications

Description:

One Side Metallised, Other Side Non Heat Sealable OPP Film for use in Lamination with Paper / Paper Board, Gift Wrapping and Decorative Application. The film exhibits excellent water vapour and gas barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with Inks during printing.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-MD
One Side Metallised, Other Side Non Heat Sealable OPP Film for use in Lamination with Paper / Paper Board, Gift Wrapping and Decorative Application. The film exhibits excellent water vapour and gas barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with Inks during printing.
Lamination with Paper / Paper Board for Various Applications like Disposable Paper Plates, File Covers, Leaflats Etc. • Gift Wrapping Applications • Other Decorative Applications

THERMAL GLOSS FINISH BOPP FILM

Application:

Non Heat Sealable Metallised Film for Sandwich Layer in Three Ply Laminate Packaging Structure.

Description:

One Side Metallised, Other Side Corona Treated Non Heat Sealable OPP Film for use as Sandwich Layer in Three Ply Laminate Packaging Structure. The film exhibits excel ent water vapour and gas barrier properties. During metal isation process film is treated with plasma for enhancing metal adhesion and barrier properties. Metal ised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The corona treated non heat sealable side is also designed for excellent anchoring to lamination adhesive.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N2-MD
One Side Metallised, Other Side Corona Treated Non Heat Sealable OPP Film for use as Sandwich Layer in Three Ply Laminate Packaging Structure. The film exhibits excel ent water vapour and gas barrier properties. During metal isation process film is treated with plasma for enhancing metal adhesion and barrier properties. Metal ised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The corona treated non heat sealable side is also designed for excellent anchoring to lamination adhesive.
Non Heat Sealable Metallised Film for Sandwich Layer in Three Ply Laminate Packaging Structure.

THERMAL GLOSS FINISH BOPP FILM

Application:

Heat Sealable Matt Metallised Film For High Speed Packaging Application.

Description:

One Side Matt Metallised, Other Side Heat Sealable OPP Film is excellent water vapour and gas barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The untreated heat sealable side exhibits excellent hot-tack and seal strength.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-MTD
One Side Matt Metallised, Other Side Heat Sealable OPP Film is excellent water vapour and gas barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. The untreated heat sealable side exhibits excellent hot-tack and seal strength.
Heat Sealable Matt Metallised Film For High Speed Packaging Application.

THERMAL GLOSS FINISH BOPP FILM

Application:

White Cavitated Heat Sealable Metallised Film for Single / Two Ply Printing Lamination Application (For Ice Cream Packaging, Labels, High Value Food Packaging Etc.)

Description:

High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. For better anchorage of inks & lamination adhesives, a primer or corona booster may be applied on metallised side before conversion. The untreated heat sealable side exhibits excellent hot-tack and seal strength.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PLD
High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. For better anchorage of inks & lamination adhesives, a primer or corona booster may be applied on metallised side before conversion. The untreated heat sealable side exhibits excellent hot-tack and seal strength.
White Cavitated Heat Sealable Metallised Film for Single / Two Ply Printing Lamination Application (For Ice Cream Packaging, Labels, High Value Food Packaging Etc.)

THERMAL GLOSS FINISH BOPP FILM

Application:

High Barrier White Cavitated Heat Sealable Metallise Ed Film For Single / Two Ply Printing Lamination Application ( for Ice Cream Packaging, Labels, High Value Food Packaging Etc).

Description:

High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single /Two Ply Packaging Structure. The film exhibits very high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with Inks and lamination adhesives. The untreated heat sealable side exhibits excellent hot-tack and seal strength.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PDB
High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single /Two Ply Packaging Structure. The film exhibits very high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with Inks and lamination adhesives. The untreated heat sealable side exhibits excellent hot-tack and seal strength.
High Barrier White Cavitated Heat Sealable Metallise Ed Film For Single / Two Ply Printing Lamination Application ( for Ice Cream Packaging, Labels, High Value Food Packaging Etc).

THERMAL GLOSS FINISH BOPP FILM

Application:

High Barrier Heat Sealable Metallised Film for Single / Two Ply Packaging Structure

Description:

High Barrier, One Side Metallized, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits very high water vapor and gas barrier properties. During metallization process film is treated with plasma for improving metal adhesion and barrier properties. Metallized side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. Untreated heat sealable side exhibits excellent hot-tack and seal strength.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-MDB
High Barrier, One Side Metallized, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits very high water vapor and gas barrier properties. During metallization process film is treated with plasma for improving metal adhesion and barrier properties. Metallized side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives. Untreated heat sealable side exhibits excellent hot-tack and seal strength.
High Barrier Heat Sealable Metallised Film for Single / Two Ply Packaging Structure

THERMAL GLOSS FINISH BOPP FILM

Application:

High Heat Seal Strength Sealable Metallised Film for Single / Two Ply Packaging Structure. Potential Replacement of Metallised CPP in few Structures.

Description:

One Side Metallised, Other Side High Heat Seal Strength Sealable OPP Film for Use in Single / Two Ply Packaging Structure. Speciality of this Film is Very High Sealing Strength and Outstanding Hot Tack Properties. Due to the Excellent Sealing Characteristics, this film can be considered as potential Replacement of Metallised CPP in Two Ply Laminating Structure. Also, this film exhibits excellent water vapour and gas barrier properties compare to Metallised CPP. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-AMD
One Side Metallised, Other Side High Heat Seal Strength Sealable OPP Film for Use in Single / Two Ply Packaging Structure. Speciality of this Film is Very High Sealing Strength and Outstanding Hot Tack Properties. Due to the Excellent Sealing Characteristics, this film can be considered as potential Replacement of Metallised CPP in Two Ply Laminating Structure. Also, this film exhibits excellent water vapour and gas barrier properties compare to Metallised CPP. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with lamination adhesives.
High Heat Seal Strength Sealable Metallised Film for Single / Two Ply Packaging Structure. Potential Replacement of Metallised CPP in few Structures.