High Transparent Barrier Films

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
J-200P0 One side PVdC coated transparent polyester packaging film. The film is printable on coated side and can be sealed coating to coating side. It has excellent moisture, oxygen and aroma barrier. 12,13,14,25,32,38 µ
  • Resistance to pasteurization
  • Excellent water, gas and aroma barrier
  • High transparency
  • Excellent dimensional stability
  • PVdC can be easily laminated with other substrates
  • Very good compatibility with NC, PVB inks
  • Suitable for flexo and gravure printing
For see through packaging application. The film is suitable for pasteurization application without losing its barrier properties and transparency.  
J-172P0 One side PVdC coated transparent polyester packaging film. The film is printable on coated side and can be sealed coating to coating. It has excellent moisture, oxygen and aroma barrier. 12,13,14 µ
  • Non-pasteurizable grade
  • Excellent water, gas and aroma barrier
  • High transparency
  • Excellent dimensional stability
  • PVdC can be easily laminated with other substrates
  • Very good compatibility with NC, PVB inks
  • Suitable for flexo and gravure printing
  • Solvent free coating
For see through packaging application. The film is suitable for non-pasteurization application.  

THERMAL GLOSS FINISH BOPP FILM

Application:

For see through packaging application. The film is suitable for pasteurization application without losing its barrier properties and transparency.

Description:

One side PVdC coated transparent polyester packaging film. The film is printable on coated side and can be sealed coating to coating side. It has excellent moisture, oxygen and aroma barrier.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-200P0
One side PVdC coated transparent polyester packaging film. The film is printable on coated side and can be sealed coating to coating side. It has excellent moisture, oxygen and aroma barrier.
For see through packaging application. The film is suitable for pasteurization application without losing its barrier properties and transparency. For packaging application where high barrier required. It can be surface or reverse printed and can be laminated with other webs. The film is printable on coated side and can be sealed coating to coating.

THERMAL GLOSS FINISH BOPP FILM

Application:

For see through packaging application. The film is suitable for non-pasteurization application.

Description:

One side PVdC coated transparent polyester packaging film. The film is printable on coated side and can be sealed coating to coating. It has excellent moisture, oxygen and aroma barrier.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-172P0
One side PVdC coated transparent polyester packaging film. The film is printable on coated side and can be sealed coating to coating. It has excellent moisture, oxygen and aroma barrier.
For see through packaging application. The film is suitable for non-pasteurization application. For packaging application where high barrier required. It can be surface or reverse printed and can be laminated with other webs. The film is printable on coated side and can be sealed coating to coating.