Transparent Non Heat Sealable

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
N1-HCF Transparent Non Heat Sealable One Side Corona Treated – Anti slip 15 to 20 µ
  • High Surface Gloss
  • Excellent Surface Treatment Retention
  • Excellent bond in Extrusion lamination at Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
Suitable for Extrusion Lamination with PP Woven Fabric; where Other Side is modified with Anti-Slip / Anti-Skid Property  

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for Extrusion Lamination with PP Woven Fabric; where Other Side is modified with Anti-Slip / Anti-Skid Property

Description:

Transparent Non Heat Sealable One Side Corona Treated – Anti slip

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-HCF
Transparent Non Heat Sealable One Side Corona Treated – Anti slip
Suitable for Extrusion Lamination with PP Woven Fabric; where Other Side is modified with Anti-Slip / Anti-Skid Property Transparent, Non Heat Sealable, One Side Corona Treated, High Glossy OPP Film for Extrusion lamination with PP woven fabric. The corona treated surface is specifically designed to suit extrusion lamination process. Untreated side is modified with anti-slip / anti-skid property