Transparent Non Heat Sealable

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
N1 -LB Transparent High Glossy High Energy Treated 25 TO 50 µ
  • Excellent Clarity
  • Excellent Surface Gloss
  • Low Haze
  • Specially Design for Surface Printing Applications
  • Excellent Anchorage and Get up of Inks on High Glossy High Energy Treated Side
  • Excellent Anchorage of Hot Melt Adhesive on Other Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
Wrap Around and Pressure Sensitive Label Applications  
N2-LB Transparent High Glossy High Energy Treated 25 TO 50 µ
  • Excellent Clarity
  • Excellent Surface Gloss
  • Low Haze
  • Specially Design for Surface Printing Applications
  • Excellent Anchorage and Get up of Inks on High Glossy High Energy Treated Side
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive on Other Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
Wrap Around and Pressure Sensitive Label Applications  

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Applications

Description:

Transparent High Glossy High Energy Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1 -LB
Transparent High Glossy High Energy Treated
Wrap Around and Pressure Sensitive Label Applications Transparent, Non Heat Sealable, High Glossy High Energy Treated OPP Film with excellent clarity, slip and antistatic properties for use in various label application. One side is high glossy high energy treated surface, specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other Side is design for anchorage with hot melt adhesives

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Applications

Description:

Transparent High Glossy High Energy Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N2-LB
Transparent High Glossy High Energy Treated
Wrap Around and Pressure Sensitive Label Applications Transparent, Non Heat Sealable, High Glossy High Energy Treated OPP Film with excellent clarity, slip and antistatic properties for use in various label application. One side is high glossy high energy treated surface, specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other Side is treated for facilitating anchorage with various hot melt and pressure sensitive adhesives.