Cavitated - Pearlized and White

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
H2-PLG White Cavitated Both Side Heat Sealable High Energy Treated High Glossy 25 TO 40 µ
  • Excellent Opacity
  • Brilliant Pearlicent White Appearance
  • High Surface Gloss
  • Specially Design for Surface Printing Applications
  • High Gloss High Energy Treatment for Facilitating Surface Printing by Flexo / Gravure Process
  • Excellent Anchorage of Inks on High Energy Treated Side
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive on Other Treated Side
  • Excellent Hot tack Properties
  • Excellent Surface Treatment Retention
  • Excellent Machinability
  • Very Good Barrier Properties
Wrap Around and Pressure Sensitive Label Application  
N2-PLG White Cavitated Non Heat Sealable High Energy Treated High Glossy 25 TO 40 µ
  • Excellent Opacity
  • Brilliant Pearlicent White Appearance
  • High Surface Gloss
  • Specially Design for Surface Printing Applications
  • High Gloss High Energy Treatment for Facilitating Surface Printing by Flexo / Gravure Process
  • Excellent Anchorage of Inks on High Energy Treated Side
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive on Other Treated Side
  • Excellent Surface Treatment Retention
  • Excellent Machinability
  • Very Good Barrier Properties
Wrap Around and Pressure Sensitive Label Application  
N1-PLG White Cavitated Non Heat Sealable High Energy Treated High Glossy 25 TO 40 µ
  • Excellent Opacity
  • Brilliant Pearlicent White Appearance
  • High Surface Gloss
  • Specially Design for Surface Printing Applications
  • High Gloss High Energy Treatment for Facilitating Surface Printing by Flexo / Gravure Process
  • Excellent Anchorage of Inks on High Energy Treated Side
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive
  • Excellent Surface Treatment Retention
  • Excellent Machinability
  • Very Good Barrier Properties
Roll-fed Wrap Around Label Application  
H2-PLW Superb White Cavitated Both Side Heat -Sealable Both Side Corona Treated 38 µ
  • Superb White & Glossy Appearance
  • Excellent Opacity
  • Low density & high yield
  • Specially Designed for Surface Printing Applications
  • One side High Corona Treated polymer specifically designed for Surface Printing by Flexo / Gravure Process
  • Printable side is designed to give excellent colour tone of the inks applied
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive on Other Treated Side
  • Excellent Stiffness of the film facilitates easy die-cut/blade-cut & machinability on labelling machine
Wrap Around and Pressure Sensitive Label Application, Where Superb White Appearance & Excellent Stiffness is required.  

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Application

Description:

White Cavitated Both Side Heat Sealable High Energy Treated High Glossy

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H2-PLG
White Cavitated Both Side Heat Sealable High Energy Treated High Glossy
Wrap Around and Pressure Sensitive Label Application White Cavitated, Both Side Heat Sealable, Both Side High Energy Treated, High Glossy OPP Film with excellent Opacity, Slip and Antistatic Properties for use in Wrap Around and Pressure Sensitive Label Applications. One side is high glossy high energy treated heat sealable surface, specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other side is treated heat sealable with excellent hot tack properties, which facilitate the closure being made with heat sealing after wrapping of the label.

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Application

Description:

White Cavitated Non Heat Sealable High Energy Treated High Glossy

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N2-PLG
White Cavitated Non Heat Sealable High Energy Treated High Glossy
Wrap Around and Pressure Sensitive Label Application White Cavitated, Non Heat Sealable, High Energy Treated, High Glossy OPP Film with excellent Opacity, Slip and Antistatic Properties for use in Wrap Around and Pressure Sensitive Label Applications. One side is high glossy high energy treated non heat sealable surface, specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other Side is treated for facilitating anchorage with various hot melt and pressure sensitive adhesives.

THERMAL GLOSS FINISH BOPP FILM

Application:

Roll-fed Wrap Around Label Application

Description:

White Cavitated Non Heat Sealable High Energy Treated High Glossy

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-PLG
White Cavitated Non Heat Sealable High Energy Treated High Glossy
Roll-fed Wrap Around Label Application White Cavitated, Non Heat Sealable, One Side High Energy Treated, High Glossy OPP Film with excellent Opacity, Slip and Antistatic Properties for use in Roll-fed Wrap Around Label Applications. High glossy high energy treated surface is specifically designed for excel ent get up and adhesion of surface printing by flexo / gravure process.

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Application, Where Superb White Appearance & Excellent Stiffness is required.

Description:

Superb White Cavitated Both Side Heat -Sealable Both Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H2-PLW
Superb White Cavitated Both Side Heat -Sealable Both Side Corona Treated
Wrap Around and Pressure Sensitive Label Application, Where Superb White Appearance & Excellent Stiffness is required. Superb White Cavitated, Both Side Heat Sealable, Both Side corona treated, superb white appearance OPP Film With excellent Opacity, Slip and Antistatic Properties for use in Wrap Around and Pressure Sensitive Label applications. One side (normally inside) is high corona treated polymer specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other side is corona treated and exhibits excellent anchorage with hot-melt and various pressure sensitive adhesives.