MET-BOPP

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
H1-PLD High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. For better anchorage of inks & lamination adhesives, a primer or corona booster may be applied on metallised side before conversion. The untreated heat sealable side exhibits excellent hot-tack and seal strength. 25,30,35,38,40,50 µ
  • Very High Water Vapour and Gas Barrier Properties
  • Excellent Opacity
  • One Side Brilliant Pearlescent White Appearance and Other Side Brilliant Metallic Lustre
  • Very High Surface Gloss
  • Low Seal Initiation Temperature
  • Excellent Hot Tack and Heat Seal Strength
  • For better anchorage of inks & lamination adhesives, a primer or corona booster may be applied on metallised side before conversion
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
White Cavitated Heat Sealable Metallised Film for Single / Two Ply Printing Lamination Application (For Ice Cream Packaging, Labels, High Value Food Packaging Etc.)  
H1-PDB High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single /Two Ply Packaging Structure. The film exhibits very high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with Inks and lamination adhesives. The untreated heat sealable side exhibits excellent hot-tack and seal strength. 25,30,35,38,40,50 µ
  • Very High Water Vapour and Gas Barrier Properties
  • Excellent Opacity
  • One Side Brilliant Pearlicent White Appearance and Other Side Brilliant Metallic Lustre
  • Very High Surface Gloss
  • Low Seal Initiation Temperature
  • Excellent Hot Tack and Heat Seal Strength
  • Excellent Surface Treatment Retention on Metallised Side
  • Excellent Anchorage of Inks and Lamination Adhesive on Metallised Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
High Barrier White Cavitated Heat Sealable Metallise Ed Film For Single / Two Ply Printing Lamination Application ( for Ice Cream Packaging, Labels, High Value Food Packaging Etc).  

THERMAL GLOSS FINISH BOPP FILM

Application:

White Cavitated Heat Sealable Metallised Film for Single / Two Ply Printing Lamination Application (For Ice Cream Packaging, Labels, High Value Food Packaging Etc.)

Description:

High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. For better anchorage of inks & lamination adhesives, a primer or corona booster may be applied on metallised side before conversion. The untreated heat sealable side exhibits excellent hot-tack and seal strength.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PLD
High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single / Two Ply Packaging Structure. The film exhibits high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. For better anchorage of inks & lamination adhesives, a primer or corona booster may be applied on metallised side before conversion. The untreated heat sealable side exhibits excellent hot-tack and seal strength.
White Cavitated Heat Sealable Metallised Film for Single / Two Ply Printing Lamination Application (For Ice Cream Packaging, Labels, High Value Food Packaging Etc.)

THERMAL GLOSS FINISH BOPP FILM

Application:

High Barrier White Cavitated Heat Sealable Metallise Ed Film For Single / Two Ply Printing Lamination Application ( for Ice Cream Packaging, Labels, High Value Food Packaging Etc).

Description:

High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single /Two Ply Packaging Structure. The film exhibits very high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with Inks and lamination adhesives. The untreated heat sealable side exhibits excellent hot-tack and seal strength.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PDB
High Barrier White Cavitated One Side Metallised, Other Side Heat Sealable OPP Film for use in Single /Two Ply Packaging Structure. The film exhibits very high water vapour and gas barrier properties. During metallisation process film is treated with plasma for improving metal adhesion and barrier properties. Metallised side is specifically designed for excellent surface treatment retention behaviour as well as very good anchorage with Inks and lamination adhesives. The untreated heat sealable side exhibits excellent hot-tack and seal strength.
High Barrier White Cavitated Heat Sealable Metallise Ed Film For Single / Two Ply Printing Lamination Application ( for Ice Cream Packaging, Labels, High Value Food Packaging Etc).