Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
J-405 J-405 grade of polyester film is a hazy and both side untreated bi-axially oriented polyester film, Film is thermally stable 12,15,19,23,25,30,36,50 µ
  • Heat Stable Film
  • Excellent Machinability
  • Intermediate Haze
  • Excellent Mechanical and Thermal Properties
  • Excellent Mechanical and Thermal Properties
Electrical applications (wire and cable insulation), FRP / GRP applications, General purpose use and other industrial applications  
J-406 J-406 grade of polyester film is a hazy and one side chemically treated bi-axially oriented polyester film. Film is thermally stable at higher temperature. 23,30,36,50 µ
  • Heat stable Film
  • Good Adhesion to Solvent base Inks and Coatings
  • Excellent Machinability
  • Excellent Mechanical and Thermal Properties
Electrical applications (wire and cable insulation), General purpose use and other industrial applications  

THERMAL GLOSS FINISH BOPP FILM

Application:

Electrical applications (wire and cable insulation), FRP / GRP applications, General purpose use and other industrial applications

Description:

J-405 grade of polyester film is a hazy and both side untreated bi-axially oriented polyester film, Film is thermally stable

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-405
J-405 grade of polyester film is a hazy and both side untreated bi-axially oriented polyester film, Film is thermally stable
Electrical applications (wire and cable insulation), FRP / GRP applications, General purpose use and other industrial applications Hazy and both side untreated bi-axially oriented polyester film, film is thermally stable

THERMAL GLOSS FINISH BOPP FILM

Application:

Electrical applications (wire and cable insulation), General purpose use and other industrial applications

Description:

J-406 grade of polyester film is a hazy and one side chemically treated bi-axially oriented polyester film. Film is thermally stable at higher temperature.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-406
J-406 grade of polyester film is a hazy and one side chemically treated bi-axially oriented polyester film. Film is thermally stable at higher temperature.
Electrical applications (wire and cable insulation), General purpose use and other industrial applications Hazy and one side chemically treated bi-axially oriented polyester film, film is thermally stable at higher temperature