Cavitated - Pearlized and White

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
H1-PLC Pearl White Low COF Low Heat Sealable One Side Corona Treated 20 TO 45 µ
  • Ultra Low COF Low Heat Seal Untreated Side
  • Excellent Opacity
  • Low Seal Initiation Temperature
  • Excel ent Hot Tack and Heat Seal Strength
  • Brilliant Pearlicent White Appearance
  • Very Good Barrier Properties
  • High Surface Gloss
  • Excel ent Surface Treatment Retention
  • Excel ent Anchorage of Inks and Lamination Adhesive on Treated Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines *Available in Inside / Outside Corona Treated, as per the requirement of the customer
Pearl White Low Heat Sealable Ultra Low COF One Side Corona Treated Film for Very High Speed Confectionary Packing Application. Also Very Useful for other single / two Ply High Speed Printing, Lamination & Pouching Applications.  
H1-PLS 20 TO 40 µ
  • Excellent Opacity
  • Low Seal Initiation Temperature
  • Excellent Hot Tack and Heat Seal Strength
  • Brilliant Pearlicent White Appearance
  • Very Good Barrier Properties
  • High Surface Gloss
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Inks and Lamination Adhesive on Treated Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
  • Available in Inside / Outside Corona Treated, as per the requirement of the customer
Pearl White Low Heat Sealable One Side Corona Treated Film for Ice Cream Packaging. Also Useful Other single / two Ply Printing Lamination Application  
H1-PL Pearl White Both Side Heat Sealable One Side Corona Treated 20 TO 40 µ
  • Excellent Opacity
  • Brilliant Pearlicent White Appearance
  • Very Good Barrier Properties
  • High Surface Gloss
  • Excellent Hot Tack and Heat Seal Strength
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Inks and Lamination Adhesive on Treated Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
  • Available in Inside / Outside Corona Treated, as per the requirement of the customer
Pearl White Both Side Heat Sealable One Side Corona Treated Film for single / two Ply Printing Lamination Application  
H1-PUL Pearl White Ultra Low Heat Sealable One Side Corona Treated 25 TO 40 µ
  • Excellent Opacity
  • Ultra Low Seal Initiation Temperature
  • Excellent Hot Tack and Heat Seal Strength
  • Brilliant Pearlicent White Appearance
Pearl White Ultra Low Heat Sealable One Side Corona Treated Film  
H1-PLG White Cavitated Both Side Heat Sealable One Side High Energy Treated High Glossy 25 TO 40 µ
  • Excellent Opacity
  • Brilliant Pearlicent White Appearance
  • High Surface Gloss
  • Specially Design for Surface Printing Applications
  • High Gloss High Energy Treatment for Facilitating Surface Printing by Flexo / Gravure Process
  • Excellent Anchorage of Inks on High Energy Treated Side
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive on Other Treated Side
  • Excellent Hot-tack Properties
  • Excellent Surface Treatment Retention
  • Excellent Machinability
  • Very Good Barrier Properties
Wrap Around and Pressure Sensitive Label Application. Also can be used for Packaging Applications  
H2-PLG White Cavitated Both Side Heat Sealable High Energy Treated High Glossy 25 TO 40 µ
  • Excellent Opacity
  • Brilliant Pearlicent White Appearance
  • High Surface Gloss
  • Specially Design for Surface Printing Applications
  • High Gloss High Energy Treatment for Facilitating Surface Printing by Flexo / Gravure Process
  • Excellent Anchorage of Inks on High Energy Treated Side
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive on Other Treated Side
  • Excellent Hot tack Properties
  • Excellent Surface Treatment Retention
  • Excellent Machinability
  • Very Good Barrier Properties
Wrap Around and Pressure Sensitive Label Application  
N1-PL Pearl White Non Heat Sealable One Side Corona Treated 18 TO 40 µ
  • Excellent White Pearl Effect
  • Excellent Surface Gloss
  • Excellent Opacity
  • Treated Side is Designed for Facilitating Surface Printing by Flexo / Gravure Process
  • Excellent Anchorage of Inks on Treated Side
  • Excellent Machinability
  • Very Good Barrier Properties
  • Suitable for Various Printing / Lamination Machines
Pearl White Non Heat Sealable One Side Corona Treated Film for Single / Two / Three Ply Printing Lamination Applications  
N2-PL Pearl White Non Heat Sealable Both Side Corona Treated 18 TO 40 µ
  • Excellent White Pearl Effect
  • Excellent Surface Gloss
  • Excellent Opacity
  • Designed for Facilitating Surface Printing by Flexo / Gravure Process
  • Excellent Anchorage of Inks and Adhesives
  • Excellent Machinability
  • Very Good Barrier Properties
  • Suitable for Various Printing / Lamination Machines
Pearl White Non Heat Sealable Both Side Corona Treated Film for Single / Two / Three Ply Printing Lamination Applications  
N2-PLG White Cavitated Non Heat Sealable High Energy Treated High Glossy 25 TO 40 µ
  • Excellent Opacity
  • Brilliant Pearlicent White Appearance
  • High Surface Gloss
  • Specially Design for Surface Printing Applications
  • High Gloss High Energy Treatment for Facilitating Surface Printing by Flexo / Gravure Process
  • Excellent Anchorage of Inks on High Energy Treated Side
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive on Other Treated Side
  • Excellent Surface Treatment Retention
  • Excellent Machinability
  • Very Good Barrier Properties
Wrap Around and Pressure Sensitive Label Application  
N1-PLG White Cavitated Non Heat Sealable High Energy Treated High Glossy 25 TO 40 µ
  • Excellent Opacity
  • Brilliant Pearlicent White Appearance
  • High Surface Gloss
  • Specially Design for Surface Printing Applications
  • High Gloss High Energy Treatment for Facilitating Surface Printing by Flexo / Gravure Process
  • Excellent Anchorage of Inks on High Energy Treated Side
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive
  • Excellent Surface Treatment Retention
  • Excellent Machinability
  • Very Good Barrier Properties
Roll-fed Wrap Around Label Application  
H2-PLW Superb White Cavitated Both Side Heat -Sealable Both Side Corona Treated 38 µ
  • Superb White & Glossy Appearance
  • Excellent Opacity
  • Low density & high yield
  • Specially Designed for Surface Printing Applications
  • One side High Corona Treated polymer specifically designed for Surface Printing by Flexo / Gravure Process
  • Printable side is designed to give excellent colour tone of the inks applied
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive on Other Treated Side
  • Excellent Stiffness of the film facilitates easy die-cut/blade-cut & machinability on labelling machine
Wrap Around and Pressure Sensitive Label Application, Where Superb White Appearance & Excellent Stiffness is required.  

THERMAL GLOSS FINISH BOPP FILM

Application:

Pearl White Low Heat Sealable Ultra Low COF One Side Corona Treated Film for Very High Speed Confectionary Packing Application. Also Very Useful for other single / two Ply High Speed Printing, Lamination & Pouching Applications.

Description:

Pearl White Low COF Low Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PLC
Pearl White Low COF Low Heat Sealable One Side Corona Treated
Pearl White Low Heat Sealable Ultra Low COF One Side Corona Treated Film for Very High Speed Confectionary Packing Application. Also Very Useful for other single / two Ply High Speed Printing, Lamination & Pouching Applications. Pearl White, Low Heat Sealable, Ultra Low COF, One Side Corona Treated OPP Film with Very Good Barrier, Outstanding Slip and Antistatic Properties for use in Single / Two Ply Printing Lamination Application, Specifically for High Speed Confectionary Packaging Application. Ultra Low COF untreated side facilitate the smooth running of film on confectionary packaging machine at minimum speed of 1200 packs/min. The corona treated side is specifically designed for excel ent adhesion of inks and lamination adhesives. Untreated side exhibits Ultra Low COF, low seal initiation temperature, excel ent hot tack and seal strength.

THERMAL GLOSS FINISH BOPP FILM

Application:

Pearl White Low Heat Sealable One Side Corona Treated Film for Ice Cream Packaging. Also Useful Other single / two Ply Printing Lamination Application

Description:

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PLS
Pearl White Low Heat Sealable One Side Corona Treated Film for Ice Cream Packaging. Also Useful Other single / two Ply Printing Lamination Application Pearl White, Low Heat Sealable, One Side Corona Treated OPP Film with Very Good Barrier, Slip and Antistatic Properties for use in Single / Two Ply Printing Lamination Application, Specifically for Ice cream Packaging Application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesives. Untreated side exhibits ultra low seal initiation temperature, excellent hot tack and seal strength

THERMAL GLOSS FINISH BOPP FILM

Application:

Pearl White Both Side Heat Sealable One Side Corona Treated Film for single / two Ply Printing Lamination Application

Description:

Pearl White Both Side Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PL
Pearl White Both Side Heat Sealable One Side Corona Treated
Pearl White Both Side Heat Sealable One Side Corona Treated Film for single / two Ply Printing Lamination Application Pearl White, Both Side Heat Sealable, One Side Corona Treated OPP Film with Very Good Barrier, Slip and Antistatic Properties for use in Single / Two Ply Printing Lamination Application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesives. Untreated side exhibits excellent hot tack and seal strength

THERMAL GLOSS FINISH BOPP FILM

Application:

Pearl White Ultra Low Heat Sealable One Side Corona Treated Film

Description:

Pearl White Ultra Low Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PUL
Pearl White Ultra Low Heat Sealable One Side Corona Treated
Pearl White Ultra Low Heat Sealable One Side Corona Treated Film Pearl White Ultra Low Heat Sealable One Side Corona Treated

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Application. Also can be used for Packaging Applications

Description:

White Cavitated Both Side Heat Sealable One Side High Energy Treated High Glossy

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-PLG
White Cavitated Both Side Heat Sealable One Side High Energy Treated High Glossy
Wrap Around and Pressure Sensitive Label Application. Also can be used for Packaging Applications White Cavitated, Both Side Heat Sealable, One Side High Energy Treated, High Glossy OPP Film with excellent Opacity, Slip and Antistatic Properties for use in Wrap Around and Pressure Sensitive Label Applications. This Film can also be used for Various Packaging Applications. One side is high glossy high energy treated heat sealable surface, specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other side is untreated heat sealable with excellent hot tack properties, which facilitate the closure being made with heat sealing after wrapping of the label.

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Application

Description:

White Cavitated Both Side Heat Sealable High Energy Treated High Glossy

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H2-PLG
White Cavitated Both Side Heat Sealable High Energy Treated High Glossy
Wrap Around and Pressure Sensitive Label Application White Cavitated, Both Side Heat Sealable, Both Side High Energy Treated, High Glossy OPP Film with excellent Opacity, Slip and Antistatic Properties for use in Wrap Around and Pressure Sensitive Label Applications. One side is high glossy high energy treated heat sealable surface, specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other side is treated heat sealable with excellent hot tack properties, which facilitate the closure being made with heat sealing after wrapping of the label.

THERMAL GLOSS FINISH BOPP FILM

Application:

Pearl White Non Heat Sealable One Side Corona Treated Film for Single / Two / Three Ply Printing Lamination Applications

Description:

Pearl White Non Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-PL
Pearl White Non Heat Sealable One Side Corona Treated
Pearl White Non Heat Sealable One Side Corona Treated Film for Single / Two / Three Ply Printing Lamination Applications Pearl White, Non Heat Sealable, One Side Corona Treated OPP Film with Very Good Barrier, Slip and Antistatic Properties for use in Single / Two Ply Printing Lamination Application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesives.

THERMAL GLOSS FINISH BOPP FILM

Application:

Pearl White Non Heat Sealable Both Side Corona Treated Film for Single / Two / Three Ply Printing Lamination Applications

Description:

Pearl White Non Heat Sealable Both Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N2-PL
Pearl White Non Heat Sealable Both Side Corona Treated
Pearl White Non Heat Sealable Both Side Corona Treated Film for Single / Two / Three Ply Printing Lamination Applications Pearl White, Non Heat Sealable, Both Side Corona Treated OPP Film with Very Good Barrier, Slip and Antistatic Properties for use in Single / Two Ply Printing Lamination Application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesives.

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Application

Description:

White Cavitated Non Heat Sealable High Energy Treated High Glossy

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N2-PLG
White Cavitated Non Heat Sealable High Energy Treated High Glossy
Wrap Around and Pressure Sensitive Label Application White Cavitated, Non Heat Sealable, High Energy Treated, High Glossy OPP Film with excellent Opacity, Slip and Antistatic Properties for use in Wrap Around and Pressure Sensitive Label Applications. One side is high glossy high energy treated non heat sealable surface, specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other Side is treated for facilitating anchorage with various hot melt and pressure sensitive adhesives.

THERMAL GLOSS FINISH BOPP FILM

Application:

Roll-fed Wrap Around Label Application

Description:

White Cavitated Non Heat Sealable High Energy Treated High Glossy

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-PLG
White Cavitated Non Heat Sealable High Energy Treated High Glossy
Roll-fed Wrap Around Label Application White Cavitated, Non Heat Sealable, One Side High Energy Treated, High Glossy OPP Film with excellent Opacity, Slip and Antistatic Properties for use in Roll-fed Wrap Around Label Applications. High glossy high energy treated surface is specifically designed for excel ent get up and adhesion of surface printing by flexo / gravure process.

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Application, Where Superb White Appearance & Excellent Stiffness is required.

Description:

Superb White Cavitated Both Side Heat -Sealable Both Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H2-PLW
Superb White Cavitated Both Side Heat -Sealable Both Side Corona Treated
Wrap Around and Pressure Sensitive Label Application, Where Superb White Appearance & Excellent Stiffness is required. Superb White Cavitated, Both Side Heat Sealable, Both Side corona treated, superb white appearance OPP Film With excellent Opacity, Slip and Antistatic Properties for use in Wrap Around and Pressure Sensitive Label applications. One side (normally inside) is high corona treated polymer specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other side is corona treated and exhibits excellent anchorage with hot-melt and various pressure sensitive adhesives.