Type Description Standard Thickness* (µ) USP Application PDF
J-450VM Bi-axially oriented one side gold shade - coated metallized polyester film. Metal surface is suitable for adhesive lamination with various substrates. 11,12 µ
  • Excellent metallised surface luster. Excellent Mechanical and thermal Properties Excellent Machinability
Decorative packaging after lamination with paper  
J-950VM Bi-axially oriented one side gold shade - coated metallized-matte polyester film. Metal surface is suitable for adhesive lamination with various substrates. 12 µ
  • Excellent matte gold appearance.
  • Excellent Mechanical and thermal Properties
  • Excellent Machinability
Decorative packaging after lamination with paper  
J-950MV Bi-axially oriented one side gold shade - coated metallized-matte polyester film. Metal surface is suitable for adhesive lamination with various substrates. 12 µ
  • Excellent Matte look of gold surface. Excellent Mechanical and thermal Properties Excellent Machinability
Decorative packaging after lamination with paper  

THERMAL GLOSS FINISH BOPP FILM

Application:

Decorative packaging after lamination with paper

Description:

Bi-axially oriented one side gold shade - coated metallized polyester film. Metal surface is suitable for adhesive lamination with various substrates.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-450VM
Bi-axially oriented one side gold shade - coated metallized polyester film. Metal surface is suitable for adhesive lamination with various substrates.
Decorative packaging after lamination with paper Metal surface is suitable for adhesive lamination with various substrates. For shelf decoration purpose For packaging of wet and dry sweets, candies, sugar confectionaries etc

THERMAL GLOSS FINISH BOPP FILM

Application:

Decorative packaging after lamination with paper

Description:

Bi-axially oriented one side gold shade - coated metallized-matte polyester film. Metal surface is suitable for adhesive lamination with various substrates.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-950VM
Bi-axially oriented one side gold shade - coated metallized-matte polyester film. Metal surface is suitable for adhesive lamination with various substrates.
Decorative packaging after lamination with paper Metal surface is suitable for adhesive lamination with various substrates. For shelf decoration purpose For packaging of wet and dry sweets, candies, sugar confectionaries etc

THERMAL GLOSS FINISH BOPP FILM

Application:

Decorative packaging after lamination with paper

Description:

Bi-axially oriented one side gold shade - coated metallized-matte polyester film. Metal surface is suitable for adhesive lamination with various substrates.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-950MV
Bi-axially oriented one side gold shade - coated metallized-matte polyester film. Metal surface is suitable for adhesive lamination with various substrates.
Decorative packaging after lamination with paper Gold surface is for decorative packaging purpose