MET-PET

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
J200M0 Normal density metallization on plain side and other side plain 8,9,10,12,23 µ
  • Standard Density
  • Standard Metal Bond Strength
  • Standard Water Vapour and Gas Barrier properties
  • Good Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application, especially for higher gloss and barrier properties.  
J200M4 High density metallization on plain surface with plasma treatment and other side plain. 12 µ
  • High Density
  • Standard Metal Bond Strength
  • High Water Vapour and Gas Barrier properties
  • Good Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application, especially for high barrier properties.  
J201M0 Normal density metallization on Corona side and other side plain 7,8,9,10,12,15,19,23,36,50 µ
  • Standard Density
  • Improved Metal Bond Strength
  • Standard Water Vapor and Gas Barrier properties
  • Good Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application, especially for higher gloss and barrier properties.  
J201M1 Normal density Metallized on plain surface and other side corona treated 8,9,10,12,15,23,36 µ
  • Standard Density
  • Standard Metal Bond Strength
  • Standard Water Vapor and Gas Barrier properties
  • Good for Printing and Lamination
  • Excellent Machinability
Suitable for flexible packaging application, especially for higher gloss and barrier properties.  
J202M0 High density Metallization on corona surface and other side plain 8,10,12 µ
  • Average Density
  • Standard Metal Bond Strength
  • Moderate Water Vapour and Gas Barrier properties
  • Standard Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application, especially for higher gloss and barrier properties.  
J202M1 High density Metallised on plain surface with plasma and other side corona treated. 10,12,36 µ
  • Average Density
  • Standard Metal Bond Strength
  • Moderate Water Vapour and Gas Barrier properties
  • Standard Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where high barrier is required  
J202M4 High density Metallization on corona surface and other side plain 8,10,12 µ
  • High Density
  • Standard Metal Bond Strength
  • Good Water Vapour and Gas Barrier properties
  • Good Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application, especially for high barrier properties requirement  
J221M0 Normal density metallization on pre-coated co polyester side and other side plain 8,10,12,23 µ
  • Standard Density
  • Good Metal Bond Strength
  • Standard Water Vapour and Gas Barrier properties
  • Standard Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where good barrier and high metal bond is required, film is not recommended for liquid / sterilization application  
J221M4 High density metallization on pre-coated co polyester side and other side plain 8,10,12 µ
  • High Density
  • Good Metal Bond Strength
  • Good Water Vapour and Gas Barrier properties
  • Standard Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where high barrier and high metal bond is required  
J222M1 Normal density Metallised on pre-coated co polyester surface and other side corona treated. 10,12,15 µ
  • Standard Density
  • Good Metal Bond Strength
  • Standard Water Vapour and Gas Barrier properties
  • Corona side good for Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where high barrier and high metal bond is required  
J222M4 High density Metallized on pre-coated co polyester surface and other side corona treated 10,12 µ
  • High Density
  • Good Metal Bond Strength
  • Good Water Vapour and Gas Barrier properties
  • Corona side Good for Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where high barrier and high metal bond is required  
J222M5 Ultra high density metallization on pre-coated co polyester side and other side corona 12 µ
  • High Density
  • Good Metal Bond Strength
  • Excellent Water Vapour and Gas Barrier properties
  • Good Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where high barrier and high metal bond is required  
J231M3 Normal density Metallised on plain surface and other side chemically pre-treated 10,12,23 µ
  • Standard Density
  • Standard Metal Bond Strength
  • Standard Water Vapour and Gas Barrier properties
  • Good for Printing and Lamination
Suitable for flexible packaging application, chemical treated side is suitable for printing  
J231M4 High density Metallised on plain surface and other side chemically pre-treated 10,12,23 µ
  • High Density
  • Standard Metal Bond Strength
  • Good Water Vapour and Gas Barrier properties
  • Good for printing and Lamination
Suitable for flexible packaging application, chemical treated side is suitable for printing.  
J232M3 Normal density Metallised on corona surface and other side chemically pre-treated. 10,12 µ
  • Standard Density
  • Standard Metal Bond Strength
  • Standard Water Vapour and Gas Barrier properties
  • Good for Printing and Lamination
Suitable for flexible packaging application, chemical treated side is suitable for printing  
J232M4 High density Metallised on corona surface and other side chemically pre-treated. 10,12 µ
  • High Density
  • Standard Metal Bond Strength
  • Standard Water Vapour and Gas Barrier properties
  • Good for printing and Lamination
Suitable for flexible packaging application, chemical treated side is suitable for printing  
J233M3 Normal density Metallised on plain surface with Plasma and other side chemically pre-treated. 8,10,12,15 µ
  • Standard Density
  • Standard Metal Bond Strength
  • Standard Water Vapour and Gas Barrier properties
  • Good for Printing with UV Curable Ink and Standard Lamination Bond Strength
Suitable for flexible packaging application, chemical treated side is good for surface printing with UV curable inks.  
J234M3 Normal density Metallized on Corona surface and other side Chemically Pre-treated. 10,12,15 µ
  • Standard Density
  • Improved Metal Bond Strength
  • Standard Water Vapour and Gas Barrier properties
  • Good for printing with UV curable ink and Lamination
Suitable for flexible packaging application, Chemical treated side is good for surface printing with UV curable inks.  
J261M0 Normal density Metallised on pre-coated chemical surface and other side plain. 10,12 µ
  • Standard Density
  • High Metal Bond Strength
  • Good Water Vapour and Gas Barrier properties
  • Standard Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where good barrier and high metal bond is required, film is recommended for liquid packaging application  
J262M1 Normal density Metallised on pre-coated chemical surface and other side corona 10,12 µ
  • Standard Density
  • High Metal Bond Strength
  • Good Water Vapour and Gas Barrier properties
  • Good Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where good barrier and high metal bond is required. Film is suitable for hot fill application also.  
J262M4 High densityx Metallized on pre-coated co polyester Surface and other side corona treated. 10,12 µ
  • High Density
  • High Metal Bond Strength
  • Good Water Vapour and Gas Barrier properties
  • Good Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where good barrier and high metal bond is required. Film is suitable for hot fill application also.  
J262M5 High density Metallized on pre-coated co polyester Surface and other side corona treated 10,12 µ
  • High Density
  • High Metal Bond Strength
  • very Good Water Vapour and Gas Barrier properties
  • Good Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where good barrier and high metal bond is required. Film is suitable for hot fill application also.  
J281M0 Normal density Metallization on chemical coated surface offer high metal adhesion performance. 12 µ
  • Standard Density
  • High Metal Bond Strength
  • Standard Water Vapour and Gas Barrier properties
  • Excellent Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where high metal bond is required. Film is suitable for hot fill applications  
J281M5 High density Metallisation on pre-coated chemical surface and other side Non treated 12 µ
  • High Density
  • Excellent Metal Bond Strength
  • Excellent Water Vapour and Gas Barrier properties
  • Excellent Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging application where high barrier and high metal bond is required. Film is suitable for hot fill applications.  
J450M0 Normal density Metallised on plain surface and other side plain. 12,13 µ
  • Standard density
  • Good Metal Bond Strength
  • High Gloss
  • Excellent Dimensional/Thermal Stability.
  • Excellent Machinability
Specially designed for Metallic yarn application.  
J500MO Normal density Metallised on plain surface and other side plain. 23,50,100,110,125,135,140,150 µ
  • Standard Density
  • Standard Metal Bond Strength
  • High Gloss
  • Standard Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging, glitter powder application, especially for higher gloss  
J530M0 Normal density Metallised on plain surface and other side plain. 50,150 µ
  • Standard Density
  • Standard Metal Bond Strength
  • Standard Lamination Bond Strength
  • Excellent Machinability
Suitable for flexible packaging, glitter powder application, especially for higher gloss  
J700M0 Normal density Metallized on plain surface and other side plain 12,23 µ
  • Standard Density
  • Isotropic Mechanical property
  • High Thermal Stability and Good Machinability.
  • Standard Metal Bond Strength
  • Good Water Vapour and Gas Barrier properties
Suitable for flexible packaging application  
J701M0 Normal density Metallized on corona treated surface and other side plain. 12,23 µ
  • Standard Density
  • Isotropic Mechanical property
  • High Thermal Stability and good Machinability.
  • Improved Metal Bond Strength
  • Good Water Vapour and Gas Barrier properties
Suitable for flexible packaging application,  
J950MO Normal density metallised direct matte polyester film with medium surface gloss. 12,23,36,50 µ
  • Standard density
  • Medium surface gloss
  • Good dimensional / thermal stability.
  • Excellent Machinability
labels and other industrial application.  
J952M1 Normal density Metallisation on translucent direct matte polyester film and other side corona treated 12,23,36,50 µ
  • Standard Density
  • Excellent Dimensional / Thermal Stability.
  • Excellent Machinability
  • Suitable for Printing
labels and other industrial application.  
J951M0 Normal density Metallised direct matte one side metallised and other side chemically coated. 12 µ
  • Standard Density
  • Good Dimensional / Thermal Stability.
  • Excellent Machinability
  • Suitable for Printing & Lamination
labels and other industrial application.  

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, especially for higher gloss and barrier properties.

Description:

Normal density metallization on plain side and other side plain

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J200M0
Normal density metallization on plain side and other side plain
Suitable for flexible packaging application, especially for higher gloss and barrier properties.

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, especially for high barrier properties.

Description:

High density metallization on plain surface with plasma treatment and other side plain.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J200M4
High density metallization on plain surface with plasma treatment and other side plain.
Suitable for flexible packaging application, especially for high barrier properties.

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, especially for higher gloss and barrier properties.

Description:

Normal density metallization on Corona side and other side plain

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J201M0
Normal density metallization on Corona side and other side plain
Suitable for flexible packaging application, especially for higher gloss and barrier properties.

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, especially for higher gloss and barrier properties.

Description:

Normal density Metallized on plain surface and other side corona treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J201M1
Normal density Metallized on plain surface and other side corona treated
Suitable for flexible packaging application, especially for higher gloss and barrier properties.

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, especially for higher gloss and barrier properties.

Description:

High density Metallization on corona surface and other side plain

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J202M0
High density Metallization on corona surface and other side plain
Suitable for flexible packaging application, especially for higher gloss and barrier properties.

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application where high barrier is required

Description:

High density Metallised on plain surface with plasma and other side corona treated.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J202M1
High density Metallised on plain surface with plasma and other side corona treated.
Suitable for flexible packaging application where high barrier is required

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, especially for high barrier properties requirement

Description:

High density Metallization on corona surface and other side plain

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J202M4
High density Metallization on corona surface and other side plain
Suitable for flexible packaging application, especially for high barrier properties requirement

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application where good barrier and high metal bond is required, film is not recommended for liquid / sterilization application

Description:

Normal density metallization on pre-coated co polyester side and other side plain

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J221M0
Normal density metallization on pre-coated co polyester side and other side plain
Suitable for flexible packaging application where good barrier and high metal bond is required, film is not recommended for liquid / sterilization application

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application where high barrier and high metal bond is required

Description:

High density metallization on pre-coated co polyester side and other side plain

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J221M4
High density metallization on pre-coated co polyester side and other side plain
Suitable for flexible packaging application where high barrier and high metal bond is required

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application where high barrier and high metal bond is required

Description:

Normal density Metallised on pre-coated co polyester surface and other side corona treated.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J222M1
Normal density Metallised on pre-coated co polyester surface and other side corona treated.
Suitable for flexible packaging application where high barrier and high metal bond is required

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application where high barrier and high metal bond is required

Description:

High density Metallized on pre-coated co polyester surface and other side corona treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J222M4
High density Metallized on pre-coated co polyester surface and other side corona treated
Suitable for flexible packaging application where high barrier and high metal bond is required

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application where high barrier and high metal bond is required

Description:

Ultra high density metallization on pre-coated co polyester side and other side corona

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J222M5
Ultra high density metallization on pre-coated co polyester side and other side corona
Suitable for flexible packaging application where high barrier and high metal bond is required

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, chemical treated side is suitable for printing

Description:

Normal density Metallised on plain surface and other side chemically pre-treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J231M3
Normal density Metallised on plain surface and other side chemically pre-treated
Suitable for flexible packaging application, chemical treated side is suitable for printing

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, chemical treated side is suitable for printing.

Description:

High density Metallised on plain surface and other side chemically pre-treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J231M4
High density Metallised on plain surface and other side chemically pre-treated
Suitable for flexible packaging application, chemical treated side is suitable for printing.

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, chemical treated side is suitable for printing

Description:

Normal density Metallised on corona surface and other side chemically pre-treated.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J232M3
Normal density Metallised on corona surface and other side chemically pre-treated.
Suitable for flexible packaging application, chemical treated side is suitable for printing

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, chemical treated side is suitable for printing

Description:

High density Metallised on corona surface and other side chemically pre-treated.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J232M4
High density Metallised on corona surface and other side chemically pre-treated.
Suitable for flexible packaging application, chemical treated side is suitable for printing

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, chemical treated side is good for surface printing with UV curable inks.

Description:

Normal density Metallised on plain surface with Plasma and other side chemically pre-treated.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J233M3
Normal density Metallised on plain surface with Plasma and other side chemically pre-treated.
Suitable for flexible packaging application, chemical treated side is good for surface printing with UV curable inks.

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for flexible packaging application, Chemical treated side is good for surface printing with UV curable inks.

Description:

Normal density Metallized on Corona surface and other side Chemically Pre-treated.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J234M3
Normal density Metallized on Corona surface and other side Chemically Pre-treated.
Suitable for flexible packaging application, Chemical treated side is good for surface printing with UV curable inks.