Transparent Non Heat Sealable

Product Table / Data Sheet

Type Description Standard Thickness* (µ) USP Application PDF
N1-AT Transparent Non Heat Sealable One Side Corona Treated 20 TO 50 µ
  • High Surface Gloss
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Various Pressure Sensitive Adhesives on Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
PRESSURE SENSITIVE ADHESIVE TAPE  
N1-TFT Transparent Non Heat Sealable One Side Flame Treated Side Corona Treated 20 TO 50 µ
  • High Surface Gloss
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Various Pressure Sensitive Adhesives on Treated Side
  • 100% Back Treatment Free
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
Pressure Sensitive Adhesive Tape  
N1-LH Transparent Non Heat Sealable One Side Corona Treated Low Haze 17 TO 50 µ
  • Low Haze
  • Excellent Surface Gloss and Transparency
  • Excellent Surface Treatment Retention
  • Excellent Adhesion of Holographic Coating and Printing Inks on Treated Side
  • Water Clear Holographic Appearance after Embossing
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
Low Haze Base Film for Holography Embossing, Textile Bags and Flower Overwrap Applications  

THERMAL GLOSS FINISH BOPP FILM

Application:

PRESSURE SENSITIVE ADHESIVE TAPE

Description:

Transparent Non Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-AT
Transparent Non Heat Sealable One Side Corona Treated
PRESSURE SENSITIVE ADHESIVE TAPE Transparent, Non Heat Sealable, One Side Corona Treated,

THERMAL GLOSS FINISH BOPP FILM

Application:

Pressure Sensitive Adhesive Tape

Description:

Transparent Non Heat Sealable One Side Flame Treated Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-TFT
Transparent Non Heat Sealable One Side Flame Treated Side Corona Treated
Pressure Sensitive Adhesive Tape Transparent, Non Heat Sealable, One Side Flame Treated, High Glossy OPP Film for use in Pressure Sensitive Adhesive Tape Manufacturing Application. The flame treated surface is specifically designed for excellent anchorage of various solvent and water based pressure sensitive adhesive used for self adhesive tape manufacturing. Untreated side is 100% back treatment free, which facilitate the trouble free unwinding of adhesive coated jumbo rolls.

THERMAL GLOSS FINISH BOPP FILM

Application:

Low Haze Base Film for Holography Embossing, Textile Bags and Flower Overwrap Applications

Description:

Transparent Non Heat Sealable One Side Corona Treated Low Haze

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-LH
Transparent Non Heat Sealable One Side Corona Treated Low Haze
Low Haze Base Film for Holography Embossing, Textile Bags and Flower Overwrap Applications Transparent, Low Haze, Non Heat Sealable, One Side Corona Treated OPP Base Film for Holography Embossing Textile Bags And Flower Overwrap Applications. The corona treated side is specifically designed for excellent adhesion of holographic coating and printing inks. Because of very low haze of the film, water clear holographic appearance exhibited by the film after embossing. High clarity and low haze of the film impart excellent aesthetic appeal for textile bags and flower overwrapping.